Ivoclar Cention N System Kit

Description

Cention N offers tooth-coloured esthetics together with high flexural strength. The new filling material belongs to the materials group of Alkasites. The patented alkaline filler increases the release of hydroxide ions to regulate the pH value during acid attacks. As a result, demineralization can be prevented. Moreover, the release of large numbers of fluoride and calcium ions forms a sound basis for the remineralization of dental enamel. The initiator system enables good chemical self-curing.

 

 

  Available in 15gm and 30 gm packs

Key Features

• Stronger than glass ionomer cement
• More esthetic than amalgam and glass ionomer cement
• Time-saving replacement of tooth structure in only four working steps

Specifications

COMPOSITION:

Cention N Liquid contains:

• Dimethacrylates, initiators
• Stabilizers and additives

Cention N Powder contains:

• Calcium fluoro-silicate glass
• Barium glass
• Calcium-barium-aluminium fluoro-silicate glass
• Iso-fillers
• Ytterbium trifluoride
• Initiators and pigments

Once mixed (Powder : Liquid 4.6:1 parts by weight, which corresponds to 1 measuring scoop of Powder + 1 drop of Liquid), Cention N contains 78.4 wt%, or 57.6 vol% of inorganic fillers. The particle size of the inorganic fillers ranges between 0.1 and 7 µm.

TECHNICAL SPECIFICATION:

• Mixing time (at 23 °C): 45–60 s
• Working time: 3 mins
• Setting time (self-curing): 5 min (from the start of mixing)

Packaging

Available in 15gm and 30 gm packs

Directions for Use

Application

1. Isolation Appropriate isolation is required.

2. Cavity preparation

2.1 Cavity preparation when using Cention N without an adhesive

When using Cention N without an adhesive, the preparation guidelines for the placement of amalgam fillings apply (retentive preparation design, resistance form). Retentive undercuts need to be prepared in all areas of the cavity. Enamel portions not supported by dentin must be avoided. In order to prevent fractures of Class II fillings, the area of the isthmus should be sufficiently deep and wide: on the occlusal/proximal aspect it should be at least 1.5 mm in depth, and on the buccal/oral aspect at least half the cuspto-cusp distance. The cavity floor should feature a bevel from the occlusal to the proximal aspect in order to reduce tension peaks. Enamel margins should not be bevelled. Subsequently, rinse the cavity with water spray to remove all the residue and dry with water- and oil-free air.

2.2 Cavity preparation when optionally using Cention N with an adhesive

The cavity is prepared according to the principles of the adhesive technique, i.e. by preserving as much of the tooth structure as possible. Do not prepare sharp internal angles or additional undercuts in caries-free areas. The geometry of the cavity is predetermined by the dimensions of the caries lesion or the old filling. Slightly bevel or round out the enamel margins using finishing diamonds (grit size 25–40 µm). Subsequently, rinse the cavity with water to remove all residue and dry with water- and oil-free air

3. Pulp protection / Base

If no adhesive is used, areas close to the pulp should be selectively coated with a calcium hydroxide preparation (e.g. ApexCal®). If an adhesive is used, a cavity liner is generally not necessary. Only in very deep cavities, selectively coat the area close to the pulp with a calcium hydroxide-based preparation (e.g. ApexCal®) and cover it with pressureresistant cement (glass ionomer cement, e.g. Vivaglass® Liner) before applying the dentin-enamel bonding agent. Do not cover other cavity walls, since they can be used to support the bond with a dentin-enamel bonding agent

4. Placing the matrix / interdental wedge

If the cavity includes proximal areas, place a matrix band and secure it with a wedge.

5. Conditioning / Applying the dentin-enamel bonding agent

When using Cention N without an adhesive, do not condition the tooth structure with phosphoric acid. Condition and apply the dentin-enamel bonding agent according to the Instructions for Use of the product in use. Ivoclar Vivadent recommends using the dentin-enamel bonding agent Tetric® N-Bond Universal or Tetric® N-Bond (in combination with phosphoric acid etching).

6. Dispensing and mixing

The mixing ratio for a small cavity is: 1 measuring scoop of Powder and 1 drop of Liquid (this corresponds to a weight ratio of 4.6:1). For larger cavities, a mixing ratio of either 2 measuring scoops of Powder and 2 drops of Liquid or 3 measuring scoops of Powder and 3 drops of Liquid should be used.

7. Finishing / Checking the occlusion

After polymerization, remove excess material with suitable tungsten carbide finishers or fine-grit diamonds. Remove proximal excess with diamond or tungsten carbide finishers or using finishing strips or flexible finishing discs. Check the occlusion and articulation and grind in the necessary adjustments to prevent premature contacts or undesired articulation paths on the surface of the restoration.

Additional Information

Country of Origin: Liechtenstein

Manufacturer:
Ivoclar Vivadent AG
Bendererstrasse 2, 9494 Schaan, Liechtenstein

Packer:
Ivoclar Vivadent AG
Bendererstrasse 2, 9494 Schaan, Liechtenstein

Imported By:
Ivoclar Vivadent India Pvt. Ltd.
Ground Floor and 1st Floor, Khandsa Village, Gurugram, Haryana, India
Phone: +91 72899 99456