3M ESPE P-60 Micro Hybrid Posterior Syringe B2

Description

• Filtek P60 posterior restorative is an esthetic light cured, radiopaque composite specifically designed for use in posterior direct or indirect restorations. Bonding to the tooth structure is accomplished by using a dental adhesive system, such as 3M™ Single Bond or 3M™ Scotchbond™ Multi-Purpose Adhesive Systems.
• The material is incrementally placed and cured in the cavity.
• The maximum increment thickness is 2.5mm.
• Each layer should be cured for 20 seconds

 FEATURES:

• Available in three shades
• Superior packability
• Fast curing-time – only 20 seconds to cure an increment of 2.5mm
• Excellent strength
• Wear resistance
• Low polymerisation shrinkage

INDICATIONS:

• Direct posterior restorations class I and II
• Sandwich technique with glass ionomer resin material
• Cusp buildups
• Core buildups
• Splinting
• Indirect posterior restorations including inlays and onlays

Key Features

• Exceptional Packability: Easily manipulated without sticking to instruments, allowing precise sculpting.
• Resistance to Slumping: Maintains its shape during application, ensuring accurate placement.
• Superior Marginal Adaptation: Seamlessly integrates with the natural tooth structure for a precise fit.
• Low Polymerization Shrinkage: Minimizes stress on the tooth and reduces the potential for patient sensitivity.
• High Wear Resistance: Ensures long-lasting restorations for durable performance.
• Fast Placement Technique: Requires only 20 seconds to cure an increment of 2.5mm, streamlining the restoration process.
• Versatile Applications: Suitable for both direct anterior and posterior restorations, core build-ups, splinting, and indirect restorations like inlays, onlays, and veneers.

Specifications

• Category	Item	Details / Value
  Ingredient	Silane treated silica	–
  	(1-methylethylidene)bis[4,1-phenyleneoxy(2-hydroxy-3,1-propanediyl)] bismethacrylate	–
  	Bisphenol A polyethylene glycol diether dimethacrylate (polymer)	–
  	Diurethane Dimethacrylate (UDMA)	–
  	Triethylene Glycol Dimethacrylate (TEGDMA)	–
  	Aluminium oxide	–
  	N,N-Dimethylbenzocaine (EDMAB)	–
  Property	Compressive Strength	395 MPa
  	Flexural Strength	155 MPa
  	Polymerization Shrinkage	2.0% vol.
  	Fracture Toughness	1.5 MPa·m¹/²
  	Filler Content	61% vol.

• Fastest Placement
• Low Shrinkage
• Excellent Wear Resistant & tear Strength

Packaging

4g syringe

Directions for Use

Preparation:

• Begin by preparing the tooth or teeth for the restoration as per standard dental procedures.
• Ensure that the tooth is clean and free of debris.

Isolation:

• Isolate the tooth or area being worked on using a dental dam or other isolation techniques to prevent contamination.

Application of the Restorative Material:

• Extrude a small amount of the 3M Espe P-60 Micro Hybrid Posterior material onto a clean, disposable mixing pad.
• Load the material onto a suitable placement instrument (e.g., a composite instrument or a dental spatula).

Placement:

• Carefully place and sculpt the material into the prepared cavity or onto the tooth surface.
• Shape and contour the material to achieve the desired anatomical form.

Light Curing:

• Cure the material using a dental curing light following the recommended curing time provided by the manufacturer. Typically, 20 seconds is required for an increment of 2.5mm.

Additional Information

Country of Origin: USA

Manufacturer:
3M ESPE Dental Products
2510 Conway Avenue, St. Paul, MN 55144-1000, USA

Packer:
3M ESPE Dental Products
2510 Conway Avenue, St. Paul, MN 55144-1000, USA

Imported & Marketed By:
3M India Limited
No. 48, South West Corner Portion in B Building B, Near Main Gate, at Toll India Logistics Pvt. Limited Compound, Puzhal, Ambattur Road, Puzhal, Chennai – 600066, Tamil Nadu, India
Phone: +91 72899 99456

Warranty & Service

• No warranty is applicable for this product